Abstract
A new A1-A2 type polymer pDTDPP-TTF containing diketopyrrolopyrrole (DPP) and 2-ethylhexyl-3-fluorothieno[3,4-b]thiophene-2-carboxylate (TTF) as the main electron-accepting building blocks has been synthesized via Suzuki cross-coupling polycondensation. The introduction of TTF as an additional electron-deficient unit significantly lowers the LUMO energy level of this DPP containing polymer to -4.37 eV which is beneficial for efficient electron injection and transport. The pDTDPP-TTF polymer shows an ultra narrow optical bandgap of 1.06 eV with a broad absorption spectra covering the visible to near infrared region of up to 1300 nm. Solution-processed OFET devices with pDTDPP-TTF as the active semiconducting layer have been fabricated with the configurations of both bottom-gate bottom-contact (BG-BC) and top-gate bottom-contact (TG-BC). The BG-BC devices with SiO2 as a dielectric exhibit ambipolar behavior with a hole and electron mobility of 1.85 × 10-4 and 3.55 × 10-5 cm2 V-1 s-1, respectively. Improved OFET performance has been achieved in TG-BC devices by using PMMA as the dielectric; balanced ambipolar charge transport is obtained with a hole and electron mobility of 6.17 × 10-3 cm2 V-1 s-1 and 3.13 × 10-3 cm2 V-1 s-1, respectively. To the best of our knowledge, our work is among the very few examples of ultra-low bandgap semiconducting polymers with balanced ambipolar charge transport properties.
Original language | English |
---|---|
Pages (from-to) | 78720-78726 |
Number of pages | 7 |
Journal | RSC Advances |
Volume | 6 |
Issue number | 82 |
DOIs | |
State | Published - 2016 |