Characterization and optimization of La0.8Sr0.2Sc0.1Mn0.9O3-δ-based composite electrodes for intermediate-temperature solid-oxide fuel cells

Yao Zheng, Ran Ran, Hongxia Gu, Rui Cai, Zongping Shao

Research output: Contribution to journalArticlepeer-review

14 Scopus citations

Abstract

Composite electrodes composed of a perovskite-type La0.8Sr0.2Sc0.1Mn0.9O3-δ (LSSM) and a fluorite-type scandium-stabilized zirconia (ScSZ) were prepared and evaluated as potential cathodes for intermediate-temperature solid-oxide fuel cells. Characterization was made by phase reaction, electrochemical impedance spectroscopy, step current polarization and I-V tests. The phase reaction between LSSM and ScSZ occurred at 1150 °C or higher; however, it had a minor effect on the electrode performance. The formation of a composite electrode led to an obvious improvement in both charge transfer and surface-related processes. With the increase of ScSZ content, the rate-limiting step of oxygen reduction reaction steadily changed from mainly a surface diffusion process to an electron transfer process. The optimal ScSZ content and sintering temperature of the electrode layer were found to be 20 wt.% and 1100-1150 °C, respectively. Under optimal conditions, an anode-supported single cell with LSSM + ScSZ composite cathode showed high power densities of ∼1211 and 386 mW cm-2 at 800 and 650 °C, respectively.

Original languageEnglish
Pages (from-to)641-648
Number of pages8
JournalJournal of Power Sources
Volume185
Issue number2
DOIs
StatePublished - 1 Dec 2008

Keywords

  • Composite cathodes
  • Electrochemical impedance spectroscopy
  • Intermediate-temperature solid-oxide fuel cells
  • LaSrScMnO
  • Oxygen reduction

Fingerprint

Dive into the research topics of 'Characterization and optimization of La0.8Sr0.2Sc0.1Mn0.9O3-δ-based composite electrodes for intermediate-temperature solid-oxide fuel cells'. Together they form a unique fingerprint.

Cite this