T1 - Construction of Hierarchical Natural Fabric Surface Structure Based on Two-Dimensional Boron Nitride Nanosheets and Its Application for Preparing Biobased Toughened Unsaturated Polyester Resin Composites
AU - Chu, Fukai
AU - Zhang, Dichang
AU - Hou, Yanbei
AU - Qiu, Shuilai
AU - Wang, Junling
AU - Hu, Weizhao
AU - Song, Lei
N1 - Publisher Copyright:
Copyright © 2018 American Chemical Society.
PY - 2018/11/21
Y1 - 2018/11/21
N2 - It has been a big challenge to prepare the unsaturated polyester resin (UPR) composites with good fire safety, interfacial quality, and impact strength in an environmentally friendly way. In this study, to improve interfacial performance of fabric-reinforced UPR composites, nontoxic two-dimensional hexagonal boron nitride (h-BN) nanosheets were assembled on the surface of ramie fabrics, where sodium alginate acts as a green dispersant to disperse h-BN sheets during the process. Then, the biobased phosphorus-containing toughening agent (PCTA) was synthesized to simultaneously improve the impact strength and fire safety of the composite. With application of h-BN nanosheets-assembled fabric (AF) and 20 wt % of PCTA, the AF/UPR@PCTA20 composite presented the maximum 41.2% decrease in the value of peak heat release rate and a maximum 17.8% decrease in the value of total heat release, which also reached V-0 rating in the vertical burning test. Meanwhile, the AF/UPR@PCTA20 composite showed an obvious increase in limiting oxygen index, from 24.0 to 29.5% compared with RF/UPR. The flame retardant mechanism was investigated from gas phase and condensed phase. Furthermore, compared to neat RF/UPR composite, the AF/UPR@PCTA20 composite showed a significant 68.8% improvement in impact strength, implying an extreme toughening effect of PCTA on UPR composites. The research provides a viable green method for the development of environmentally friendly UPR composites in the future.
AB - It has been a big challenge to prepare the unsaturated polyester resin (UPR) composites with good fire safety, interfacial quality, and impact strength in an environmentally friendly way. In this study, to improve interfacial performance of fabric-reinforced UPR composites, nontoxic two-dimensional hexagonal boron nitride (h-BN) nanosheets were assembled on the surface of ramie fabrics, where sodium alginate acts as a green dispersant to disperse h-BN sheets during the process. Then, the biobased phosphorus-containing toughening agent (PCTA) was synthesized to simultaneously improve the impact strength and fire safety of the composite. With application of h-BN nanosheets-assembled fabric (AF) and 20 wt % of PCTA, the AF/UPR@PCTA20 composite presented the maximum 41.2% decrease in the value of peak heat release rate and a maximum 17.8% decrease in the value of total heat release, which also reached V-0 rating in the vertical burning test. Meanwhile, the AF/UPR@PCTA20 composite showed an obvious increase in limiting oxygen index, from 24.0 to 29.5% compared with RF/UPR. The flame retardant mechanism was investigated from gas phase and condensed phase. Furthermore, compared to neat RF/UPR composite, the AF/UPR@PCTA20 composite showed a significant 68.8% improvement in impact strength, implying an extreme toughening effect of PCTA on UPR composites. The research provides a viable green method for the development of environmentally friendly UPR composites in the future.
KW - composite interphase
KW - fire safety
KW - impact strength
KW - natural fabric
KW - phosphorus-containing biobased toughening agent
KW - unsaturated polyester resin
UR - http://www.scopus.com/inward/record.url?scp=85056970103&partnerID=8YFLogxK
U2 - 10.1021/acsami.8b15355
DO - 10.1021/acsami.8b15355
M3 - 文章
C2 - 30365884
AN - SCOPUS:85056970103
SN - 1944-8244
VL - 10
SP - 40168
EP - 40179
JO - ACS Applied Materials and Interfaces
JF - ACS Applied Materials and Interfaces
IS - 46
ER -