Design of PTFE/PP multilayer composite membrane as mask filter layer with steady filtration efficiency and high dust holding capacity

Junwei Wu, Yuanyuan Rao, Bin Lin, Hongjia Zhou, Qun Zhou, Chaonan Xu, Shasha Feng, Zhaoxiang Zhong, Weihong Xing

Research output: Contribution to journalArticlepeer-review

7 Scopus citations

Abstract

Currently, commercially available mask filter materials, such as electrostatic electret polypropylene (PP) melt-blown cloth and polytetrafluoroethylene (PTFE) nanofiber membranes, always suffer a compromise between filtration efficiency and dust holding capacity, when used alone during air purification. In this study, a novel multilayer composite membrane was designed by thermally laminating a PP melt-blown filter layer (as the dust-holding layer) and a PTFE (Polytetrafluoroethylene) nanofiber layer (as the filtration layer), to improve filtration stability and capacity. The performance of the composite membrane was examined in relation to the effect of key laminating parameters (i.e., temperature, pressure and speed) on the dust holding capacity, filtration efficiency and resistance. NaCl aerosol was used as the model dust source. Results show that the composite membrane, prepared at a lamination temperature of 120 °C, a lamination pressure of 0.2 MPa and a lamination speed of 4 m/min, had a dust-holding capacity of 12.21 g/m2, which was over six times higher than that of the PTFE nanofiber membrane alone. During ten repeated cycles of NaCl aerosol filtration, water washing and alcohol disinfection, the composite membrane exhibited a steady filtration efficiency of above 99.9% over the NaCl aerosol. Meanwhile, the dust holding capacity was maintained above 8 g/m2 over the multiple cycles, while the resistance was smaller than 70 Pa.

Original languageEnglish
Article number124782
JournalSeparation and Purification Technology
Volume326
DOIs
StatePublished - 1 Dec 2023

Keywords

  • High dust capacity
  • Laminating process
  • PTFE nanofiber Membrane
  • Reusable

Fingerprint

Dive into the research topics of 'Design of PTFE/PP multilayer composite membrane as mask filter layer with steady filtration efficiency and high dust holding capacity'. Together they form a unique fingerprint.

Cite this