T1 - Direct Synthesis of MoS2 Nanosheets in Reduced Graphene Oxide Nanoscroll for Enhanced Photodetection
AU - Wu, Zhikang
AU - Li, Feifei
AU - Li, Xiya
AU - Yang, Yang
AU - Huang, Xiao
AU - Li, Hai
N1 - Publisher Copyright:
© 2022 by the authors. Licensee MDPI, Basel, Switzerland.
PY - 2022/5/1
Y1 - 2022/5/1
N2 - Due to their unique tubular and spiral structure, graphene and graphene oxide nanoscrolls (GONS) have shown extensive applications in various fields. However, it is still a challenge to improve the optoelectronic application of graphene and GONS because of the zero bandgap of graphene. Herein, ammonium tetrathiomolybdate ((NH4)2MoS4) was firstly wrapped into the ((NH4)2MoS4@GONS) by molecular combing the mixture of (NH4)2MoS4 and GO solution on hydrophobic substrate. After thermal annealing, the (NH4)2MoS4 and GO were converted to MoS2 nanosheets and reduced GO (RGO) simultaneously, and, thus, the MoS2@RGONS was obtained. Raman spectroscopy and high-resolution transmission electron microscopy were used to confirm the formation of MoS2 nanosheets among the RGONS. The amount of MoS2 wrapped in RGONS increased with the increasing height of GONS, which is confirmed by the atomic force microscopy and Raman spectroscopy. The as-prepared MoS2@RGONS showed much better photoresponse than the RGONS under visible light. The photocurrent-to-dark current ratios of photodetectors based on MoS2@RGONS are ~570, 360 and 140 under blue, red and green lasers, respectively, which are 81, 144 and 35 times of the photodetectors based on RGONS. Moreover, the MoS2@RGONS-based photodetector exhibited good power-dependent photoresponse. Our work indicates that the MoS2@RGONS is expected to be a promising material in the fields of optoelectronic devices and flexible electronics.
AB - Due to their unique tubular and spiral structure, graphene and graphene oxide nanoscrolls (GONS) have shown extensive applications in various fields. However, it is still a challenge to improve the optoelectronic application of graphene and GONS because of the zero bandgap of graphene. Herein, ammonium tetrathiomolybdate ((NH4)2MoS4) was firstly wrapped into the ((NH4)2MoS4@GONS) by molecular combing the mixture of (NH4)2MoS4 and GO solution on hydrophobic substrate. After thermal annealing, the (NH4)2MoS4 and GO were converted to MoS2 nanosheets and reduced GO (RGO) simultaneously, and, thus, the MoS2@RGONS was obtained. Raman spectroscopy and high-resolution transmission electron microscopy were used to confirm the formation of MoS2 nanosheets among the RGONS. The amount of MoS2 wrapped in RGONS increased with the increasing height of GONS, which is confirmed by the atomic force microscopy and Raman spectroscopy. The as-prepared MoS2@RGONS showed much better photoresponse than the RGONS under visible light. The photocurrent-to-dark current ratios of photodetectors based on MoS2@RGONS are ~570, 360 and 140 under blue, red and green lasers, respectively, which are 81, 144 and 35 times of the photodetectors based on RGONS. Moreover, the MoS2@RGONS-based photodetector exhibited good power-dependent photoresponse. Our work indicates that the MoS2@RGONS is expected to be a promising material in the fields of optoelectronic devices and flexible electronics.
KW - MoS2@reduced graphene oxide nanoscroll
KW - ammonium tetrathiomolybdate
KW - photodetection
KW - photosensitivity
KW - thermal annealing
UR - http://www.scopus.com/inward/record.url?scp=85129426693&partnerID=8YFLogxK
U2 - 10.3390/nano12091581
DO - 10.3390/nano12091581
M3 - 文章
AN - SCOPUS:85129426693
SN - 2079-4991
VL - 12
JO - Nanomaterials
JF - Nanomaterials
IS - 9
M1 - 1581
ER -