Integrating coral-like morphology into cyano-containing carbon nitride towards efficient photocatalytic H₂ evolution and Cr(Ⅵ) reduction

The incomplete polymerization of graphite carbon nitride (g-C₃N₄) due to the kinetic problems resulted in its high recombination rate of photo-generated electron-hole pairs. Hence, cyano-containing carbon nitride with coral-like morphology (CCCN) was prepared by the molten salt method with heptazine-based melem as precursor, which presented excellent separation rate of photo-generated electron-hole pairs. SEM exhibited that CCCN owned coral-like morphology which exposed ample active sites and enhanced the capture ability of visible light while FT-IR and XPS demonstrated that cyano groups appearing in coral-like carbon nitride enhanced the separation rate of photo-induced charge carriers. The synergistic effect of coral-like morphology and cyano groups endowed CCCN-15% with superior performance of both the photocatalytic H₂ evolution (4207 μmol h⁻¹ g⁻¹) and Cr (Ⅵ) reduction (k = 0.059 min⁻¹), approximately 16.8 and 6.0 times that of g-C₃N₄, which was comparable among the similar materials. Density functional theory calculation (DFT) revealed that cyano groups decreased the bandgap and strengthened the activation degree of reaction substrate, which enhanced the thermodynamic driving force and the interaction between catalyst and substrate. This work provided a potential strategy for both the renewable energy generation and environmental restoration.