Kinetic performance of hydrogen generation enhanced by AlCl₃ via hydrolysis of MgH₂ prepared by hydriding combustion synthesis

Magnesium hydride (MgH₂) is a very promising hydrogen storage material and it has been paid more and more attention on the application of supplying hydrogen on-board because the theoretical hydrogen yield is up to 1703 mL/g when it reacts with water. However, the hydrolysis reaction is inhibited rapidly by the passivation layer of Mg(OH)₂ formed on the surface of MgH₂. This paper reports that high purity MgH₂ (∼98.7 wt%) can be readily obtained by the process of hydriding combustion synthesis (HCS) and the hydrogen generation via hydrolysis of the as-prepared HCSed MgH₂ can be dramatically enhanced by the addition of AlCl₃ in hydrolysis solutions. An excellent kinetics of hydrogen generation of 1487 mL/g in 10 min and 1683 mL/g in 17 min at 303 K was achieved for the MgH₂-0.5 M AlCl₃ system, in which the theoretical hydrogen yield (1685 mL/g) of the HCSed product was nearly reached. The mechanism of the hydrolysis kinetics enhancement was demonstrated by the generation of a large amounts of H⁺ from the Al³⁺ hydrolysis and the pitting corrosion (Cl⁻) of the Mg(OH)₂ layer wrapped on the surface of MgH₂ even at a low temperature. In addition, the apparent activation energies for the MgH₂ hydrolysis in the 0.1 M AlCl₃ and 0.5 M AlCl₃ solutions are decreased to 34.68 kJ/mol and 21.64 kJ/mol, respectively, being far superior to that of reported in deionized water (58.06 kJ/mol). The results suggest that MgH₂ + AlCl₃ system may be used as a promising hydrogen generation system in practical application of supplying hydrogen on-board.