Preparations and characterizations of tunable and multicolored electrochromic copolymers derived from a novel star-shaped monomer and BEDOT-V

A novel star-shaped monomer 1,3,5-Tri[2-(3,4-ethylenedioxythien-2-yl)vin-1- yl]benzene (TEDOT-V-B) was synthesized by Wittig coupling reaction. The copolymers with BEDOT-V at different feed ratios were prepared onto the ITO-coated glass by cyclic voltammetry (CV) method and the electrochromic properties were reported. The influences of different feed ratios on the spectroelectrochemical and kinetic properties were investigated. Spectroelectrochemical studies indicated that the maximum absorption wavelengths of the copolymer films bathochromically shifted with feed ratios. In addition, the copolymers had tunable and low band gaps. When the feed ratio of BEDOT-V-B/BEDOT-V was 1:3, the copolymer film showed the fastest oxidation switching time of 0.9s (567 nm) and 0.9s (967 nm) and the fastest reduction switching time of 0.8s (567 nm) and 0.9s (967 nm). Compared with PBEDOT-V, the copolymers showed tunable and multicolored electrochromism through feed ratios and the RGB colors were achieved. Additionally, the surface morphology of the copolymer film was investigated by scanning electron microscope (SEM).