Air exposure improving hydrogen desorption behavior of Mg–Ni-based hydrides

It is well established that H₂O and O₂ have an inauspicious influence on hydrogen reactivity of hydrogen storage alloys. In this work, an unexpected improvement of the desorption behavior was discovered by just exposing the magnesium rich Mg–Ni hydrides into the air for a certain period. Upon an exposure duration of 4 months, the dehydrogenation peak and onset temperature were sharply lowered by 150 °C and 130 °C. Furthermore, the air-exposed sample could quickly absorb 3.08 wt% H₂ and desorb 2.81 wt% H₂ within 400 s at 300 °C. Besides the refinement of the powders due to the spontaneous hydrolysis reaction, the in-situ formed magnesium hydroxide layer and Ni are thought to be responsible for the remarkable improvement. This work gives interesting insights that the self-generating surface passivation is not necessarily harmful in the solid-state hydrogen storage area, especially for the cases where active sites of catalysis are present.