Characterization and electrochemical properties of carbon-coated Li ₄Ti₅O₁₂ prepared by a citric acid sol-gel method

Since carbon coating can effectively improve electrical wiring of Li ₄Ti₅O₁₂ and thus enhance its high rate performance, a novel and simple citric acid sol-gel method for in situ carbon coating is employed in this study. The effects of the amount of the carbon source in the starting xerogel on the particle size, the resistance and the electrochemical performance of the synthesized Li₄Ti ₅O₁₂ samples are systematically studied. The physical and electrochemical properties of the obtained samples have been characterized by XRD, TG-DSC, SEM, TEM, BET, A.C. impedance, galvanostatically charge-discharge and cyclic voltammetry tests. The results show that the initial amount of the carbon source in the starting xerogel is a critical factor which determines the content of the coated carbon and the pore volume, therefore governs the high rate performance of the Li₄Ti₅O₁₂/C composites. The Li₄Ti₅O₁₂/C composite with in situ carbon coating of 3.5 wt% exhibits the best electrochemical performance which delivers delithiation capacities of 143.6 and 133.5 mAh g^-1 with fairly stable cycling performance even after 50 cycles at 0.5C and 1C rate, respectively.