Corrosion and its control in redox-flow batteries

Xuecheng Chen; Yuping Wu; Rudolf Holze

doi:10.1007/978-3-031-57012-4_21

Corrosion and its control in redox-flow batteries

Xuecheng Chen, Yuping Wu, Rudolf Holze

科研成果: 书/报告/会议事项章节 › 章节 › 同行评审

摘要

Corrosion of metals and carbon in their numerous forms used as functional and auxiliary materials in redox flow batteries is an unwelcome cause of performance degradation, malfunction, and even failure of these devices. The high chemical reactivities of employed redox systems add to the problems. Reported observations, causes of corrosion, and options to control and avoid corrosion are presented in this chapter.

源语言	英语
主期刊名	Corrosion and Degradation in Fuel Cells, Supercapacitors and Batteries
出版商	Springer Nature
页	485-496
页数	12
ISBN（电子版）	9783031570124
ISBN（印刷版）	9783031570117
DOI	https://doi.org/10.1007/978-3-031-57012-4_21
出版状态	已出版 - 12 6月 2024
已对外发布	是

访问文件

10.1007/978-3-031-57012-4_21

其它文件与链接

链接到 Scopus 的出版物

引用此

@inbook{3cdecde88c164aedbcd6bcf966672027,

title = "Corrosion and its control in redox-flow batteries",

abstract = "Corrosion of metals and carbon in their numerous forms used as functional and auxiliary materials in redox flow batteries is an unwelcome cause of performance degradation, malfunction, and even failure of these devices. The high chemical reactivities of employed redox systems add to the problems. Reported observations, causes of corrosion, and options to control and avoid corrosion are presented in this chapter.",

keywords = "Carbon corrosion, Corrosion, Materials degradation, Metal corrosion, RFB, Redox flow batteries",

author = "Xuecheng Chen and Yuping Wu and Rudolf Holze",

year = "2024",

month = jun,

day = "12",

doi = "10.1007/978-3-031-57012-4_21",

language = "英语",

isbn = "9783031570117",

pages = "485--496",

booktitle = "Corrosion and Degradation in Fuel Cells, Supercapacitors and Batteries",

publisher = "Springer Nature",

}

TY - CHAP

T1 - Corrosion and its control in redox-flow batteries

AU - Chen, Xuecheng

AU - Wu, Yuping

AU - Holze, Rudolf

PY - 2024/6/12

Y1 - 2024/6/12

N2 - Corrosion of metals and carbon in their numerous forms used as functional and auxiliary materials in redox flow batteries is an unwelcome cause of performance degradation, malfunction, and even failure of these devices. The high chemical reactivities of employed redox systems add to the problems. Reported observations, causes of corrosion, and options to control and avoid corrosion are presented in this chapter.

AB - Corrosion of metals and carbon in their numerous forms used as functional and auxiliary materials in redox flow batteries is an unwelcome cause of performance degradation, malfunction, and even failure of these devices. The high chemical reactivities of employed redox systems add to the problems. Reported observations, causes of corrosion, and options to control and avoid corrosion are presented in this chapter.

KW - Carbon corrosion

KW - Corrosion

KW - Materials degradation

KW - Metal corrosion

KW - RFB

KW - Redox flow batteries

UR - http://www.scopus.com/inward/record.url?scp=85209701007&partnerID=8YFLogxK

U2 - 10.1007/978-3-031-57012-4_21

DO - 10.1007/978-3-031-57012-4_21

M3 - 章节

AN - SCOPUS:85209701007

SN - 9783031570117

SP - 485

EP - 496

BT - Corrosion and Degradation in Fuel Cells, Supercapacitors and Batteries

PB - Springer Nature

ER -

Corrosion and its control in redox-flow batteries

摘要

访问文件

其它文件与链接

指纹

引用此