T1 - Deep eutectic solvents appended to UiO-66 type metal organic frameworks
T2 - Preserved open metal sites and extra adsorption sites for CO 2 capture
AU - Li, Zhong
AU - Sun, Wenzhe
AU - Chen, Chong
AU - Guo, Qirui
AU - Li, Xue
AU - Gu, Mengwei
AU - Feng, Nengjie
AU - Ding, Jing
AU - Wan, Hui
AU - Guan, Guofeng
N1 - Publisher Copyright:
© 2019
PY - 2019/6/30
Y1 - 2019/6/30
N2 - Targeting CO 2 capture at low pressure due to the partial pressure of CO 2 in flue gases (0.01 MPa–0.02 MPa), a facile method was constructed to build functional UiO-66 structure via mixing ligands of terephthalic acid and 1,2,4-benzenetricarboxylic acid. The free -COOH from 1,2,4-benzenetricarboxylic acid could graft quantitative and dispersive deep eutectic solvents onto UiO-66 with reserved open metal sites for CO 2 adsorption. Compared to 1,3,5-benzenetricarboxylic acid, mixing ligands by 1,2,4-benzenetricarboxylic acid preserved the stability of UiO-66 structure, which was more suitable for CO 2 capture from flue gases. The active -NH 2 and -OH groups from incorporated DES synergized with the intrinsic open metal sites to enhance the CO 2 uptake at low pressure and improve adsorption selectivity of CO 2 /N 2 . At 298 K, the CO 2 uptake of DES@UiO-66-COOH(0.05) was increased by 26% at 1 bar and 50% at 0.15 bar compared to UiO-66. In addition, the selectivity of CO 2 /N 2 for DES@UiO-66-COOH(0.05) was 24.7 times as high as UiO-66 at low pressure. The strong interaction between guest CO 2 and modified UiO-66 was confirmed by higher isosteric heats of adsorption (Q st ) for DES-appended UiO-66. Even so, the sample could be regenerated at 373 K and vacuum, and could be recycled without drop of CO 2 uptake after 6 times.
AB - Targeting CO 2 capture at low pressure due to the partial pressure of CO 2 in flue gases (0.01 MPa–0.02 MPa), a facile method was constructed to build functional UiO-66 structure via mixing ligands of terephthalic acid and 1,2,4-benzenetricarboxylic acid. The free -COOH from 1,2,4-benzenetricarboxylic acid could graft quantitative and dispersive deep eutectic solvents onto UiO-66 with reserved open metal sites for CO 2 adsorption. Compared to 1,3,5-benzenetricarboxylic acid, mixing ligands by 1,2,4-benzenetricarboxylic acid preserved the stability of UiO-66 structure, which was more suitable for CO 2 capture from flue gases. The active -NH 2 and -OH groups from incorporated DES synergized with the intrinsic open metal sites to enhance the CO 2 uptake at low pressure and improve adsorption selectivity of CO 2 /N 2 . At 298 K, the CO 2 uptake of DES@UiO-66-COOH(0.05) was increased by 26% at 1 bar and 50% at 0.15 bar compared to UiO-66. In addition, the selectivity of CO 2 /N 2 for DES@UiO-66-COOH(0.05) was 24.7 times as high as UiO-66 at low pressure. The strong interaction between guest CO 2 and modified UiO-66 was confirmed by higher isosteric heats of adsorption (Q st ) for DES-appended UiO-66. Even so, the sample could be regenerated at 373 K and vacuum, and could be recycled without drop of CO 2 uptake after 6 times.
KW - Deep eutectic solvents
KW - Isosteric heat of adsorption
KW - Selective CO adsorption
KW - UiO-66
UR - http://www.scopus.com/inward/record.url?scp=85062476420&partnerID=8YFLogxK
U2 - 10.1016/j.apsusc.2019.03.030
DO - 10.1016/j.apsusc.2019.03.030
M3 - 文章
AN - SCOPUS:85062476420
SN - 0169-4332
VL - 480
SP - 770
EP - 778
JO - Applied Surface Science
JF - Applied Surface Science
ER -