Effects of sintering atmospheres on sintering behavior, electrical conductivity and oxygen permeability of mixed-conducting membranes

Effects of sintering atmospheres on properties of SrCo_0.4Fe_0.5Zr_0.1O_3-δ mixed-conducting membranes were in detail studied in terms of sintering behavior, electrical conductivity and oxygen permeability. The sintering atmospheres were 100% N₂, 79% N₂-21% O₂, 60% N₂-40% O₂, 40% N₂-60% O₂, 20% N₂-80% O₂ and 100% O₂ (in vol.%), and the prepared membranes were correspondingly denoted as S-0, S-21, S-40, S-60, S-80 and S-100, respectively. It was found that the properties of membranes were strongly dependent on the sintering atmosphere. As the oxygen partial pressure in the sintering atmosphere (P_O2) increased, sintering ability, electrical conductivity and oxygen permeability decreased at first, which was in the order of S-0 > S-21 > S-40. However, as P_O2 increased further, sintering ability, electrical conductivity and oxygen permeability increased gradually: S-40 < S-60 < S-80 < S-100. And the S-100 membrane had the best sintering ability, electrical conductivity and oxygen permeability in all membranes.