Enhancing the hydrophilicity and water permeability of polypropylene membranes by nitric acid activation and metal oxide deposition

Activation by nitric acid oxidation has been combined with atomic layer deposition (ALD) to modify microporous polypropylene (PP) membranes. Nitric acid oxidation with prewetting of t-butanol generates active groups on the inert surface of PP membranes. Metal oxides including Al₂O₃ and TiO₂ are subsequently ALD-deposited on the activated membrane. Nitric acid oxidation is a mild approach to activate PP membranes. A short immersion in nitric acid for 10min is able to generate oxygen/nitrogen-containing active species on the membrane surface, which leads to an evident increase (38%) in the membrane permeability. The mechanical stability and the integrity of the porous structure are well preserved after activation. Surface elemental analyses and microscopy observations confirm the successful deposition of metal oxides thin layers onto the activated membranes. In the deposition of either Al₂O₃ or TiO₂, the hydrophilicity of the deposited membranes is continuously improved with increasing ALD cycles, resulting in further increase in water flux. After 100 ALD cycles, the flux is doubled compared to that of the bare membrane. Al₂O₃ is more efficient in enhancing the hydrophilicity and permeation than TiO₂ under identical deposition conditions because of the faster growth of Al₂O₃ on the activated PP surface.