Fabrication and luminescent properties of highly transparent Er3Al5O12 ceramics

Song Hu; Xianpeng Qin; Xiaoxia Liu; Guohong Zhou; Chunhua Lu; Shiwei Wang; Zhongzi Xu

doi:10.1016/j.optmat.2016.05.018

Fabrication and luminescent properties of highly transparent Er₃Al₅O₁₂ ceramics

Song Hu, Xianpeng Qin, Xiaoxia Liu, Guohong Zhou, Chunhua Lu, Shiwei Wang, Zhongzi Xu

材料科学与工程学院

科研成果: 期刊稿件 › 文章 › 同行评审

8 引用（Scopus）

摘要

Highly transparent Er₃Al₅O₁₂ (ErAG) ceramic was fabricated by a solid-state reactive sintering method under vacuum. The optical property, microstructure and up-conversion luminescence of the ErAG ceramic were investigated. For the 3 mm thick sample, the in-line transmittance at the wavelength of 3000 nm and 425 nm were about 84% and 81%, respectively, which was very close to the theoretical transmittance of the Er₃Al₅O₁₂ single crystal. Micrograph of the ErAG transparent ceramic exhibited a pore-free structure and the density of the ceramic was measured to be 6.38 g/cm³. Average grain size of the ceramic was about 9 μm. When pumped by a 980 nm laser diodes (LD), strong green and red emission in the ErAG ceramic was observed from the photoluminescence (PL) spectrum. The luminescent properties of the ceramic under the excitation of LD with various pumping power were investigated.

源语言	英语
页（从-至）	86-89
页数	4
期刊	Optical Materials
卷	71
DOI	https://doi.org/10.1016/j.optmat.2016.05.018
出版状态	已出版 - 9月 2017

访问文件

10.1016/j.optmat.2016.05.018

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{a6e26e861c72492bbce68a56a3e45b96,

title = "Fabrication and luminescent properties of highly transparent Er3Al5O12 ceramics",

abstract = "Highly transparent Er3Al5O12 (ErAG) ceramic was fabricated by a solid-state reactive sintering method under vacuum. The optical property, microstructure and up-conversion luminescence of the ErAG ceramic were investigated. For the 3 mm thick sample, the in-line transmittance at the wavelength of 3000 nm and 425 nm were about 84% and 81%, respectively, which was very close to the theoretical transmittance of the Er3Al5O12 single crystal. Micrograph of the ErAG transparent ceramic exhibited a pore-free structure and the density of the ceramic was measured to be 6.38 g/cm3. Average grain size of the ceramic was about 9 μm. When pumped by a 980 nm laser diodes (LD), strong green and red emission in the ErAG ceramic was observed from the photoluminescence (PL) spectrum. The luminescent properties of the ceramic under the excitation of LD with various pumping power were investigated.",

keywords = "ErAlO, Microstructure, Transparent ceramics, Upconversion luminescence",

author = "Song Hu and Xianpeng Qin and Xiaoxia Liu and Guohong Zhou and Chunhua Lu and Shiwei Wang and Zhongzi Xu",

note = "Publisher Copyright: {\textcopyright} 2016 Elsevier B.V.",

year = "2017",

month = sep,

doi = "10.1016/j.optmat.2016.05.018",

language = "英语",

volume = "71",

pages = "86--89",

journal = "Optical Materials",

issn = "0925-3467",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - Fabrication and luminescent properties of highly transparent Er3Al5O12 ceramics

AU - Hu, Song

AU - Qin, Xianpeng

AU - Liu, Xiaoxia

AU - Zhou, Guohong

AU - Lu, Chunhua

AU - Wang, Shiwei

AU - Xu, Zhongzi

PY - 2017/9

Y1 - 2017/9

N2 - Highly transparent Er3Al5O12 (ErAG) ceramic was fabricated by a solid-state reactive sintering method under vacuum. The optical property, microstructure and up-conversion luminescence of the ErAG ceramic were investigated. For the 3 mm thick sample, the in-line transmittance at the wavelength of 3000 nm and 425 nm were about 84% and 81%, respectively, which was very close to the theoretical transmittance of the Er3Al5O12 single crystal. Micrograph of the ErAG transparent ceramic exhibited a pore-free structure and the density of the ceramic was measured to be 6.38 g/cm3. Average grain size of the ceramic was about 9 μm. When pumped by a 980 nm laser diodes (LD), strong green and red emission in the ErAG ceramic was observed from the photoluminescence (PL) spectrum. The luminescent properties of the ceramic under the excitation of LD with various pumping power were investigated.

AB - Highly transparent Er3Al5O12 (ErAG) ceramic was fabricated by a solid-state reactive sintering method under vacuum. The optical property, microstructure and up-conversion luminescence of the ErAG ceramic were investigated. For the 3 mm thick sample, the in-line transmittance at the wavelength of 3000 nm and 425 nm were about 84% and 81%, respectively, which was very close to the theoretical transmittance of the Er3Al5O12 single crystal. Micrograph of the ErAG transparent ceramic exhibited a pore-free structure and the density of the ceramic was measured to be 6.38 g/cm3. Average grain size of the ceramic was about 9 μm. When pumped by a 980 nm laser diodes (LD), strong green and red emission in the ErAG ceramic was observed from the photoluminescence (PL) spectrum. The luminescent properties of the ceramic under the excitation of LD with various pumping power were investigated.

KW - ErAlO

KW - Microstructure

KW - Transparent ceramics

KW - Upconversion luminescence

UR - http://www.scopus.com/inward/record.url?scp=84966710338&partnerID=8YFLogxK

U2 - 10.1016/j.optmat.2016.05.018

DO - 10.1016/j.optmat.2016.05.018

M3 - 文章

AN - SCOPUS:84966710338

SN - 0925-3467

VL - 71

SP - 86

EP - 89

JO - Optical Materials

JF - Optical Materials

ER -

Fabrication and luminescent properties of highly transparent Er3Al5O12 ceramics

摘要

访问文件

其它文件与链接

指纹

引用此

Fabrication and luminescent properties of highly transparent Er₃Al₅O₁₂ ceramics