Growth of SiC as Binder to Adhere Diamond Particle and Tribological Properties of Diamond Particles Coated SiC

Shengjie Yu; Zhaofeng Chen; Yang Wang; Shuwei Hu; Ruiying Luo; Sheng Cui

doi:10.1016/j.jmst.2015.07.009

Growth of SiC as Binder to Adhere Diamond Particle and Tribological Properties of Diamond Particles Coated SiC

Shengjie Yu, Zhaofeng Chen, Yang Wang, Shuwei Hu, Ruiying Luo, Sheng Cui

材料科学与工程学院

科研成果: 期刊稿件 › 文章 › 同行评审

16 引用（Scopus）

摘要

The purpose of this work was to grow SiC as binder to adhere diamond particles to graphite substrate by low pressure chemical vapor deposition (LPCVD) at 1100 °C and 100 Pa using methyltrichlorosilane (MTS: CH₃SiCl₃) as precursor. The composite coatings on graphite substrates were analyzed by various techniques. Results show that a dense SiC coating with a cloud-cluster shape was formed both on the diamond particles and the substrate after deposition. The thermal stress (290.6 MPa) strengthened the interfacial bonding between the diamond particle and the SiC coating, which is advantageous for the purpose of adhering diamond particles to graphite substrate. The applied load of sliding wear test was found to affect not only the friction coefficient, but also the wear surface morphology. With increasing loads, the asperity penetration was high and the friction coefficient decreased.

源语言	英语
页（从-至）	1133-1138
页数	6
期刊	Journal of Materials Science and Technology
卷	31
期	11
DOI	https://doi.org/10.1016/j.jmst.2015.07.009
出版状态	已出版 - 11月 2015

访问文件

10.1016/j.jmst.2015.07.009

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{4dfc10178ce1483795f51b02959d6ec4,

title = "Growth of SiC as Binder to Adhere Diamond Particle and Tribological Properties of Diamond Particles Coated SiC",

abstract = "The purpose of this work was to grow SiC as binder to adhere diamond particles to graphite substrate by low pressure chemical vapor deposition (LPCVD) at 1100 °C and 100 Pa using methyltrichlorosilane (MTS: CH3SiCl3) as precursor. The composite coatings on graphite substrates were analyzed by various techniques. Results show that a dense SiC coating with a cloud-cluster shape was formed both on the diamond particles and the substrate after deposition. The thermal stress (290.6 MPa) strengthened the interfacial bonding between the diamond particle and the SiC coating, which is advantageous for the purpose of adhering diamond particles to graphite substrate. The applied load of sliding wear test was found to affect not only the friction coefficient, but also the wear surface morphology. With increasing loads, the asperity penetration was high and the friction coefficient decreased.",

keywords = "Diamond particle, LPCVD (low pressure chemical vapor deposition), SiC, Tribological performance",

author = "Shengjie Yu and Zhaofeng Chen and Yang Wang and Shuwei Hu and Ruiying Luo and Sheng Cui",

note = "Publisher Copyright: {\textcopyright} 2015.",

year = "2015",

month = nov,

doi = "10.1016/j.jmst.2015.07.009",

language = "英语",

volume = "31",

pages = "1133--1138",

journal = "Journal of Materials Science and Technology",

issn = "1005-0302",

publisher = "Chinese Society of Metals",

number = "11",

}

TY - JOUR

T1 - Growth of SiC as Binder to Adhere Diamond Particle and Tribological Properties of Diamond Particles Coated SiC

AU - Yu, Shengjie

AU - Chen, Zhaofeng

AU - Wang, Yang

AU - Hu, Shuwei

AU - Luo, Ruiying

AU - Cui, Sheng

PY - 2015/11

Y1 - 2015/11

N2 - The purpose of this work was to grow SiC as binder to adhere diamond particles to graphite substrate by low pressure chemical vapor deposition (LPCVD) at 1100 °C and 100 Pa using methyltrichlorosilane (MTS: CH3SiCl3) as precursor. The composite coatings on graphite substrates were analyzed by various techniques. Results show that a dense SiC coating with a cloud-cluster shape was formed both on the diamond particles and the substrate after deposition. The thermal stress (290.6 MPa) strengthened the interfacial bonding between the diamond particle and the SiC coating, which is advantageous for the purpose of adhering diamond particles to graphite substrate. The applied load of sliding wear test was found to affect not only the friction coefficient, but also the wear surface morphology. With increasing loads, the asperity penetration was high and the friction coefficient decreased.

AB - The purpose of this work was to grow SiC as binder to adhere diamond particles to graphite substrate by low pressure chemical vapor deposition (LPCVD) at 1100 °C and 100 Pa using methyltrichlorosilane (MTS: CH3SiCl3) as precursor. The composite coatings on graphite substrates were analyzed by various techniques. Results show that a dense SiC coating with a cloud-cluster shape was formed both on the diamond particles and the substrate after deposition. The thermal stress (290.6 MPa) strengthened the interfacial bonding between the diamond particle and the SiC coating, which is advantageous for the purpose of adhering diamond particles to graphite substrate. The applied load of sliding wear test was found to affect not only the friction coefficient, but also the wear surface morphology. With increasing loads, the asperity penetration was high and the friction coefficient decreased.

KW - Diamond particle

KW - LPCVD (low pressure chemical vapor deposition)

KW - SiC

KW - Tribological performance

UR - http://www.scopus.com/inward/record.url?scp=84947491648&partnerID=8YFLogxK

U2 - 10.1016/j.jmst.2015.07.009

DO - 10.1016/j.jmst.2015.07.009

M3 - 文章

AN - SCOPUS:84947491648

SN - 1005-0302

VL - 31

SP - 1133

EP - 1138

JO - Journal of Materials Science and Technology

JF - Journal of Materials Science and Technology

IS - 11

ER -

Growth of SiC as Binder to Adhere Diamond Particle and Tribological Properties of Diamond Particles Coated SiC

摘要

访问文件

其它文件与链接

指纹

引用此