Hydriding combustion synthesis of Mg-CaNi₅ composites

The composites of Mg-x wt.% CaNi₅ (x = 20, 30 and 50) were prepared by hydriding combustion synthesis (HCS) and the phase evolution during HCS as well as the hydriding properties of the products were investigated. It was found that Mg reacted with CaNi₅ forming Mg₂Ni and Ca during the heating period of HCS. Afterwards, the resultant Mg₂Ni and Ca as well as the remnant Mg reacted with hydrogen during the cooling period. The lower platform in the P-C isotherms corresponds to the hydriding of Mg, and the higher one corresponds to Mg₂Ni. With the increase of the content of CaNi₅ from 20 to 50 wt.%, the hydrogen content of the HCS products increases at first and then decreases. The Mg-30 wt.% CaNi₅ composite has the maximum hydrogen capacity of 4.74 wt.%, and it can absorb 3.51 wt.% of hydrogen in the first hydriding process without activation.