Improvement in oil resistance of room temperature-vulcanized polysiloxane rubber via blending with self-synthetic fluorosilicone

Bo Li, Shuangjun Chen, Jun Zhang

科研成果: 期刊稿件文章同行评审

3 引用 (Scopus)

摘要

In this work, different contents of vinyl-terminated fluorosilicone oil (VFS oil) were blended with room temperature-vulcanized (RTV) polydimethylsiloxane (PDMS). Via rheological detection, the addition of VFS oil could increase the viscosities of VFS/PDMS/silicon dioxide (SiO2) blends, probably due to the interaction between incorporated fluorine atom and silanol on the surfaces of SiO2. The additional "structuring effect" was reduced by enhancing the shearing rate of the mixed gums containing VFS oil and the obvious shear-thinning property was helpful for enhancing the processability. The curing process and cross-linking degree test of VFS/PDMS/SiO2 blends suggested that the VFS oil could reduce the curing time and the induction time, but did not play a positive role in the cure depth using a platinum catalyst. Mechanical property tests showed that the VFS oil did not increase the tensile strength and elongation at break, and the hardness slightly decreased with increasing VFS oil content. The oil resistance property test showed that the oil resistance of the polysiloxane rubber was well improved by the incorporation of the VFS oil containing the functional group -CH2CH2CF3.

源语言英语
页(从-至)695-709
页数15
期刊Journal of Elastomers and Plastics
46
8
DOI
出版状态已出版 - 20 12月 2014

指纹

探究 'Improvement in oil resistance of room temperature-vulcanized polysiloxane rubber via blending with self-synthetic fluorosilicone' 的科研主题。它们共同构成独一无二的指纹。

引用此