Microstructure and Mechanical Properties of (TiB₂ + SiC) Reinforced Ti₃SiC₂ Composites Synthesized by In Situ Hot Pressing

Fully dense (TiB₂ + SiC) reinforced Ti₃SiC₂ composites with 15 vol% TiB₂ and 0–15 vol% SiC were designed and synthesized by in situ reaction hot pressing. The increase in SiC content promoted densification and significantly inhibited the growth of Ti₃SiC₂ grains. The in situ incorporated TiB₂ and SiC reinforcements showed columnar and equiaxed grains, respectively, providing a strengthening–toughening effect by the synergistic action of particulate reinforcement, grain's pulling out, “self-reinforcement,” crack deflection, and grain refining. A maximum bending strength of 881 MPa and a fracture toughness of 9.24 MPam^1/2 were obtained at 10 vol% SiC. The Vickers hardness of the composites increased monotonously from 9.6 to 12.5 GPa.