On the creep fracture toughness of 21/4Cr1Mo steel

Fu Zhen Xuan; Shan Ng Tu; Zheng Dong Wang; Jian Ming Gong

doi:10.4028/0-87849-978-4.1464

On the creep fracture toughness of 21/4Cr1Mo steel

Fu Zhen Xuan, Shan Ng Tu, Zheng Dong Wang, Jian Ming Gong

机械与动力工程学院

科研成果: 期刊稿件 › 文章 › 同行评审

8 引用（Scopus）

摘要

To assess the failure risk of high temperature structures, it is essential to obtain the creep fracture toughness of materials. In the present paper, Creep crack growth (CCG) tests for 21/4Cr1Mo steel have been carried out by utilizing the side grooved compact tension (CT) specimen and direct current (DC) electrical potential technique. The material parameter of creep fracture toughness, K_mat^c, were obtained from analysis of 11 CCG tests at temperatures of 500 and 565°C. It has been found that for 21/4Cr1Mo steel K_mat^c decreases with increasing time and increases with elevating temperature. For this reason, the value of K_mat ^c at lower temperature or longer service time can be used to extract a conservative result in the high temperature defect assessment where the accurate value of K_mat^c is unavailable. It is also validated from this test that the proposed formula by Ainsworth et al can be adopted in practice.

源语言	英语
页（从-至）	1464-1469
页数	6
期刊	Key Engineering Materials
卷	297-300 III
DOI	https://doi.org/10.4028/0-87849-978-4.1464
出版状态	已出版 - 2005

访问文件

10.4028/0-87849-978-4.1464

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{891cb2753fe54f9ba1fe457898606f70,

title = "On the creep fracture toughness of 21/4Cr1Mo steel",

abstract = "To assess the failure risk of high temperature structures, it is essential to obtain the creep fracture toughness of materials. In the present paper, Creep crack growth (CCG) tests for 21/4Cr1Mo steel have been carried out by utilizing the side grooved compact tension (CT) specimen and direct current (DC) electrical potential technique. The material parameter of creep fracture toughness, Kmatc, were obtained from analysis of 11 CCG tests at temperatures of 500 and 565°C. It has been found that for 21/4Cr1Mo steel Kmatc decreases with increasing time and increases with elevating temperature. For this reason, the value of Kmat c at lower temperature or longer service time can be used to extract a conservative result in the high temperature defect assessment where the accurate value of Kmatc is unavailable. It is also validated from this test that the proposed formula by Ainsworth et al can be adopted in practice.",

keywords = "21/4Cr1Mo steel, Creep crack growth test, Creep fracture toughness, High temperature",

author = "Xuan, {Fu Zhen} and Tu, {Shan Ng} and Wang, {Zheng Dong} and Gong, {Jian Ming}",

year = "2005",

doi = "10.4028/0-87849-978-4.1464",

language = "英语",

volume = "297-300 III",

pages = "1464--1469",

journal = "Key Engineering Materials",

issn = "1013-9826",

publisher = "Trans Tech Publications Ltd",

}

TY - JOUR

T1 - On the creep fracture toughness of 21/4Cr1Mo steel

AU - Xuan, Fu Zhen

AU - Tu, Shan Ng

AU - Wang, Zheng Dong

AU - Gong, Jian Ming

PY - 2005

Y1 - 2005

N2 - To assess the failure risk of high temperature structures, it is essential to obtain the creep fracture toughness of materials. In the present paper, Creep crack growth (CCG) tests for 21/4Cr1Mo steel have been carried out by utilizing the side grooved compact tension (CT) specimen and direct current (DC) electrical potential technique. The material parameter of creep fracture toughness, Kmatc, were obtained from analysis of 11 CCG tests at temperatures of 500 and 565°C. It has been found that for 21/4Cr1Mo steel Kmatc decreases with increasing time and increases with elevating temperature. For this reason, the value of Kmat c at lower temperature or longer service time can be used to extract a conservative result in the high temperature defect assessment where the accurate value of Kmatc is unavailable. It is also validated from this test that the proposed formula by Ainsworth et al can be adopted in practice.

AB - To assess the failure risk of high temperature structures, it is essential to obtain the creep fracture toughness of materials. In the present paper, Creep crack growth (CCG) tests for 21/4Cr1Mo steel have been carried out by utilizing the side grooved compact tension (CT) specimen and direct current (DC) electrical potential technique. The material parameter of creep fracture toughness, Kmatc, were obtained from analysis of 11 CCG tests at temperatures of 500 and 565°C. It has been found that for 21/4Cr1Mo steel Kmatc decreases with increasing time and increases with elevating temperature. For this reason, the value of Kmat c at lower temperature or longer service time can be used to extract a conservative result in the high temperature defect assessment where the accurate value of Kmatc is unavailable. It is also validated from this test that the proposed formula by Ainsworth et al can be adopted in practice.

KW - 21/4Cr1Mo steel

KW - Creep crack growth test

KW - Creep fracture toughness

KW - High temperature

UR - http://www.scopus.com/inward/record.url?scp=33646002404&partnerID=8YFLogxK

U2 - 10.4028/0-87849-978-4.1464

DO - 10.4028/0-87849-978-4.1464

M3 - 文章

AN - SCOPUS:33646002404

SN - 1013-9826

VL - 297-300 III

SP - 1464

EP - 1469

JO - Key Engineering Materials

JF - Key Engineering Materials

ER -

On the creep fracture toughness of 21/4Cr1Mo steel

摘要

访问文件

其它文件与链接

指纹

引用此