Porous SiC–Si₃N₄ composite ceramics with excellent EMW absorption property prepared by gelcasting using DMAA

The porous SiC–Si₃N₄ composite ceramics with good EMW absorption properties were prepared by combination of gelcasting and carbothermal reduction. The pre-oxidation of Si₃N₄ powders significantly improved the rheological properties of slurries (0.06 Pa s at 103.92 s⁻¹) and also suppressed the generation of NH₃ and N₂ from Si₃N₄ hydrolysis and reaction between Si₃N₄ and initiator APS, thereby reducing the pore defects in green bodies and enhancing mechanical properties with a maximum value of 42.88 MPa. With the extension of oxidation time from 0 h to 10 h, the porosity and pore size of porous SiC–Si₃N₄ composite ceramics increased from approximately 41.86% and 1.0–1.5 μm to 46.33% and ~200 μm due to the production of CO, N₂ and gaseous SiO, while the sintering shrinkage decreased from 16.24% to 10.50%. With oxidation time of 2 h, the Si₂N₂O fibers formed in situ by the reaction of Si₃N₄ and amorphous SiO₂ effectively enhanced the mechanical properties, achieving the highest flexural strength of 129.37 MPa and fracture toughness of 4.25 MPa m^1/2. Compared with monolithic Si₃N₄ ceramics, the electrical conductivity, relative permittivity and dielectric loss were significantly improved by the in-situ introduced PyC from the pyrolysis of three-dimensional network DMAA-MBAM gel in green bodies and the SiC from the carbothermal reduction reaction between PyC and SiO₂ and Si₃N₄. The porous SiC–Si₃N₄ composite ceramics prepared by the unoxidized Si₃N₄ powders demonstrated the optimal EMW absorption properties with reflection loss of −22.35 dB at 8.37 GHz and 2 mm thickness, corresponding to the effective bandwidth of 8.20–9.29 GHz, displaying great application potential in EMW absorption fields.