Surfactant-free microwave-assisted hydrothermal synthesis of BaMoO ₄ hierarchical self-assemblies and enhanced photoluminescence properties

BaMoO ₄ with 3D hierarchical multilayer disk-like and nest-like architectures self-assembled from 2D nanosheets was successfully synthesized via a microwave-assisted hydrothermal route without any surfactant. The as-prepared products were characterized by X-ray powder diffractometer (XRD), scanning electron microscope (SEM), field emission transmission electron microscope (FE-TEM), and photoluminescence (PL) spectrometer. The results show that the reaction parameters, including pH value, reactant concentration, and molar ratio of [Ba2+]/[MoO42-], played important roles on the morphologies of the final products. And the formation mechanism of 3D hierarchical architectures is a stepwise oriented aggregation-based self-assembly process. The superstructure characteristic of 3D nest-like BaMoO ₄ architecture was observed in HRTEM image and the corresponding fast Fourier transform (FFT) for the first time, and the superlattice reflections with non-integer indices occurred around the subcell reflections at ±1/6(2a ^-+2c ^-). Room temperature photoluminescence spectra of 3D BaMoO ₄ architectures reveal a strong and broad blue emission, and the 3D nest-like architectures own the enhanced intensity than multilayer disks.