Synthesis of silicalite-1 membranes with high ethanol permeation in ultradilute solution containing fluoride

Xiaoliang Zhang; Meihua Zhu; Rongfei Zhou; Xiangshu Chen; Hidetoshi Kita

doi:10.1016/j.seppur.2011.08.009

Synthesis of silicalite-1 membranes with high ethanol permeation in ultradilute solution containing fluoride

Xiaoliang Zhang, Meihua Zhu, Rongfei Zhou, Xiangshu Chen, Hidetoshi Kita

科研成果: 期刊稿件 › 文章 › 同行评审

36 引用（Scopus）

摘要

Defect free silicalite-1 membranes were successfully prepared on the surface of tubular mullite supports in ultradilute solution containing fluoride by hydrothermal synthesis. The typical molar composition of synthesis solutions was 1SiO₂:0.2TPABr:0.2TPAOH:0.15NH₄F:800H₂O. The results of X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM) of zeolite membranes were confirmed that the outer surface of support was fully covered with a randomly oriented and intergrown silicalite zeolite layer. The membrane prepared at 180 °C for 20 h showed high ethanol permselectivity for separation of ethanol/water mixtures. The flux and separation factor are achieved to 2.85 kg m^-2 h^-1 and 60 for 5 wt.% ethanol/water mixture at 60 °C, respectively.

源语言	英语
页（从-至）	480-484
页数	5
期刊	Separation and Purification Technology
卷	81
期	3
DOI	https://doi.org/10.1016/j.seppur.2011.08.009
出版状态	已出版 - 10 10月 2011
已对外发布	是

访问文件

10.1016/j.seppur.2011.08.009

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{feb835123f9241b7898c966f6f9e5b7e,

title = "Synthesis of silicalite-1 membranes with high ethanol permeation in ultradilute solution containing fluoride",

abstract = "Defect free silicalite-1 membranes were successfully prepared on the surface of tubular mullite supports in ultradilute solution containing fluoride by hydrothermal synthesis. The typical molar composition of synthesis solutions was 1SiO2:0.2TPABr:0.2TPAOH:0.15NH4F:800H2O. The results of X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM) of zeolite membranes were confirmed that the outer surface of support was fully covered with a randomly oriented and intergrown silicalite zeolite layer. The membrane prepared at 180 °C for 20 h showed high ethanol permselectivity for separation of ethanol/water mixtures. The flux and separation factor are achieved to 2.85 kg m-2 h-1 and 60 for 5 wt.% ethanol/water mixture at 60 °C, respectively.",

keywords = "Ethanol/water mixture separation, Fluoride, Hydrothermal synthesis, Silicalite membrane, Ultradilute solution",

author = "Xiaoliang Zhang and Meihua Zhu and Rongfei Zhou and Xiangshu Chen and Hidetoshi Kita",

year = "2011",

month = oct,

day = "10",

doi = "10.1016/j.seppur.2011.08.009",

language = "英语",

volume = "81",

pages = "480--484",

journal = "Separation and Purification Technology",

issn = "1383-5866",

publisher = "Elsevier B.V.",

number = "3",

}

TY - JOUR

T1 - Synthesis of silicalite-1 membranes with high ethanol permeation in ultradilute solution containing fluoride

AU - Zhang, Xiaoliang

AU - Zhu, Meihua

AU - Zhou, Rongfei

AU - Chen, Xiangshu

AU - Kita, Hidetoshi

PY - 2011/10/10

Y1 - 2011/10/10

N2 - Defect free silicalite-1 membranes were successfully prepared on the surface of tubular mullite supports in ultradilute solution containing fluoride by hydrothermal synthesis. The typical molar composition of synthesis solutions was 1SiO2:0.2TPABr:0.2TPAOH:0.15NH4F:800H2O. The results of X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM) of zeolite membranes were confirmed that the outer surface of support was fully covered with a randomly oriented and intergrown silicalite zeolite layer. The membrane prepared at 180 °C for 20 h showed high ethanol permselectivity for separation of ethanol/water mixtures. The flux and separation factor are achieved to 2.85 kg m-2 h-1 and 60 for 5 wt.% ethanol/water mixture at 60 °C, respectively.

AB - Defect free silicalite-1 membranes were successfully prepared on the surface of tubular mullite supports in ultradilute solution containing fluoride by hydrothermal synthesis. The typical molar composition of synthesis solutions was 1SiO2:0.2TPABr:0.2TPAOH:0.15NH4F:800H2O. The results of X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM) of zeolite membranes were confirmed that the outer surface of support was fully covered with a randomly oriented and intergrown silicalite zeolite layer. The membrane prepared at 180 °C for 20 h showed high ethanol permselectivity for separation of ethanol/water mixtures. The flux and separation factor are achieved to 2.85 kg m-2 h-1 and 60 for 5 wt.% ethanol/water mixture at 60 °C, respectively.

KW - Ethanol/water mixture separation

KW - Fluoride

KW - Hydrothermal synthesis

KW - Silicalite membrane

KW - Ultradilute solution

UR - http://www.scopus.com/inward/record.url?scp=84864758456&partnerID=8YFLogxK

U2 - 10.1016/j.seppur.2011.08.009

DO - 10.1016/j.seppur.2011.08.009

M3 - 文章

AN - SCOPUS:84864758456

SN - 1383-5866

VL - 81

SP - 480

EP - 484

JO - Separation and Purification Technology

JF - Separation and Purification Technology

IS - 3

ER -

Synthesis of silicalite-1 membranes with high ethanol permeation in ultradilute solution containing fluoride

摘要

访问文件

其它文件与链接

指纹

引用此