Influencing factors on low-temperature deNOx performance of Mn-La-Ce-Ni-Ox/PPS catalytic filters applied for cement kiln

Bo Yang; Da Hai Zheng; Yue Song Shen; Yun Shun Qiu; Bing Li; Yan Wei Zeng; Shu Bao Shen; She Min Zhu

doi:10.1016/j.jiec.2014.09.022

Influencing factors on low-temperature deNO_x performance of Mn-La-Ce-Ni-O_x/PPS catalytic filters applied for cement kiln

Bo Yang, Da Hai Zheng, Yue Song Shen, Yun Shun Qiu, Bing Li, Yan Wei Zeng, Shu Bao Shen, She Min Zhu

材料科学与工程学院

Nanjing Tech University

科研成果: 期刊稿件 › 文章 › 同行评审

30 引用（Scopus）

摘要

Effects of catalyst loading amount, reaction temperature, O₂ concentration, NH₃/NO molar ratio and SO₂ on low-temperature catalytic performance of the Mn-La-Ce-Ni-O_x (Mn/La/Ce/Ni=2.5:2.5:1:1 in mol)/PPS for NH₃-SCR of NO were mainly studied. Results showed that the filter with catalyst loading amount of 250g/m² obtained more than 95% NO removal efficiency at 200°C under filtration velocity of 1m/min. The NO removal efficiency was still above 85% by injecting 300ppm SO₂ at 200°C. Anyway, the Mn-La-Ce-Ni-O_x/PPS catalytic filter is promising to achieve the expectation of simultaneous removing particulate and NO_x from low-sulfur flue gas in cement kiln.

源语言	英语
页（从-至）	148-152
页数	5
期刊	Journal of Industrial and Engineering Chemistry
卷	24
DOI	https://doi.org/10.1016/j.jiec.2014.09.022
出版状态	已出版 - 25 4月 2015

访问文件

10.1016/j.jiec.2014.09.022

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{5b13fe6eaf614cafa60704d2ee9572bf,

title = "Influencing factors on low-temperature deNOx performance of Mn-La-Ce-Ni-Ox/PPS catalytic filters applied for cement kiln",

abstract = "Effects of catalyst loading amount, reaction temperature, O2 concentration, NH3/NO molar ratio and SO2 on low-temperature catalytic performance of the Mn-La-Ce-Ni-Ox (Mn/La/Ce/Ni=2.5:2.5:1:1 in mol)/PPS for NH3-SCR of NO were mainly studied. Results showed that the filter with catalyst loading amount of 250g/m2 obtained more than 95% NO removal efficiency at 200°C under filtration velocity of 1m/min. The NO removal efficiency was still above 85% by injecting 300ppm SO2 at 200°C. Anyway, the Mn-La-Ce-Ni-Ox/PPS catalytic filter is promising to achieve the expectation of simultaneous removing particulate and NOx from low-sulfur flue gas in cement kiln.",

keywords = "Catalytic filter, DeNO, Mn-La-Ce-Ni-O/PPS",

author = "Bo Yang and Zheng, {Da Hai} and Shen, {Yue Song} and Qiu, {Yun Shun} and Bing Li and Zeng, {Yan Wei} and Shen, {Shu Bao} and Zhu, {She Min}",

note = "Publisher Copyright: {\textcopyright} 2014 The Korean Society of Industrial and Engineering Chemistry.",

year = "2015",

month = apr,

day = "25",

doi = "10.1016/j.jiec.2014.09.022",

language = "英语",

volume = "24",

pages = "148--152",

journal = "Journal of Industrial and Engineering Chemistry",

issn = "1226-086X",

publisher = "Korean Society of Industrial Engineering Chemistry",

}

TY - JOUR

T1 - Influencing factors on low-temperature deNOx performance of Mn-La-Ce-Ni-Ox/PPS catalytic filters applied for cement kiln

AU - Yang, Bo

AU - Zheng, Da Hai

AU - Shen, Yue Song

AU - Qiu, Yun Shun

AU - Li, Bing

AU - Zeng, Yan Wei

AU - Shen, Shu Bao

AU - Zhu, She Min

PY - 2015/4/25

Y1 - 2015/4/25

N2 - Effects of catalyst loading amount, reaction temperature, O2 concentration, NH3/NO molar ratio and SO2 on low-temperature catalytic performance of the Mn-La-Ce-Ni-Ox (Mn/La/Ce/Ni=2.5:2.5:1:1 in mol)/PPS for NH3-SCR of NO were mainly studied. Results showed that the filter with catalyst loading amount of 250g/m2 obtained more than 95% NO removal efficiency at 200°C under filtration velocity of 1m/min. The NO removal efficiency was still above 85% by injecting 300ppm SO2 at 200°C. Anyway, the Mn-La-Ce-Ni-Ox/PPS catalytic filter is promising to achieve the expectation of simultaneous removing particulate and NOx from low-sulfur flue gas in cement kiln.

AB - Effects of catalyst loading amount, reaction temperature, O2 concentration, NH3/NO molar ratio and SO2 on low-temperature catalytic performance of the Mn-La-Ce-Ni-Ox (Mn/La/Ce/Ni=2.5:2.5:1:1 in mol)/PPS for NH3-SCR of NO were mainly studied. Results showed that the filter with catalyst loading amount of 250g/m2 obtained more than 95% NO removal efficiency at 200°C under filtration velocity of 1m/min. The NO removal efficiency was still above 85% by injecting 300ppm SO2 at 200°C. Anyway, the Mn-La-Ce-Ni-Ox/PPS catalytic filter is promising to achieve the expectation of simultaneous removing particulate and NOx from low-sulfur flue gas in cement kiln.

KW - Catalytic filter

KW - DeNO

KW - Mn-La-Ce-Ni-O/PPS

UR - http://www.scopus.com/inward/record.url?scp=84930083133&partnerID=8YFLogxK

U2 - 10.1016/j.jiec.2014.09.022

DO - 10.1016/j.jiec.2014.09.022

M3 - 文章

AN - SCOPUS:84930083133

SN - 1226-086X

VL - 24

SP - 148

EP - 152

JO - Journal of Industrial and Engineering Chemistry

JF - Journal of Industrial and Engineering Chemistry

ER -

Influencing factors on low-temperature deNOx performance of Mn-La-Ce-Ni-Ox/PPS catalytic filters applied for cement kiln

摘要

访问文件

其它文件与链接

指纹

引用此

Influencing factors on low-temperature deNO_x performance of Mn-La-Ce-Ni-O_x/PPS catalytic filters applied for cement kiln