Preparation and microwave absorbing properties of nano-rod barium ferrite

Guo Xuan Xiong, Hai Qing Huang, Zhi Bin Zhang, Min Deng

科研成果: 期刊稿件文章同行评审

3 引用 (Scopus)

摘要

The nano-rod of barium ferrite was made of iron nitrate and barium nitrate as raw materials by combustion method of sol-gel and self-propagation. The composition, morphology and magnetic properties of barium ferrite nano-rod were characterized by X-ray diffraction analysis, transmission electron microscopy and vibrating sample magnetometer. The cement-based composite absorption materials of doping barium ferrite nano-rod was prepared, and its microwave absorbing properties were measured by reflection method. The results indicate that the average particle size and length of barium ferrite nano-rod are 40-60 nm and 100 nm respectively, the saturation magnetization and coercivity are 49.87 A·m2/kg and 63.1 A/m. When the contents of barium ferrite nano-rod in cement reaches 1.83% (by mass) and thickness of specimen is 20 mm, the least reflectivity of cement-based composite is -16.78 dB and bandwidth for -10 dB reaches 6 GHz in 2-18 GHz frequency range.

源语言英语
页(从-至)645-648
页数4
期刊Jianzhu Cailiao Xuebao/Journal of Building Materials
14
5
DOI
出版状态已出版 - 10月 2011

指纹

探究 'Preparation and microwave absorbing properties of nano-rod barium ferrite' 的科研主题。它们共同构成独一无二的指纹。

引用此