Silver-modified Ba_0.5Sr_0.5Co_0.8Fe _0.2O_3-δ as cathodes for a proton conducting solid-oxide fuel cell

Electrochemical performance of silver-modified Ba_0.5Sr _0.5Co_0.8Fe_0.2O_3-δ (BSCF-Ag) as oxygen reduction electrodes for a protonic intermediate-temperature solid-oxide fuel cell (SOFC-H⁺) with BaZr_0.1Ce_0.8Y _0.1O₃ (BZCY) electrolyte was investigated. The BSCF-Ag electrodes were prepared by impregnating the porous BSCF electrode with AgNO₃ solution followed by reducing with hydrazine and then firing at 850 °C for 1 h. The 3 wt.% silver-modified BSCF (BSCF-3Ag) electrode showed an area specific resistance of 0.25 Ω cm² at 650 °C in dry air, compared to around 0.55 Ω cm² for a pure BSCF electrode. The activation energy was also reduced from 119 kJ mol^-1 for BSCF to only 84 kJ mol^-1 for BSCF-3Ag. Anode-supported SOFC-H⁺ with a BZCY electrolyte and a BSCF-3Ag cathode was fabricated. Peak power density up to 595 mW cm^-2 was achieved at 750 °C for a cell with 35 μm thick electrolyte operating on hydrogen fuel, higher than around 485 mW cm^-2 for a similar cell with BSCF cathode. However, at reduced temperatures, water had a negative effect on the oxygen reduction over BSCF-Ag electrode, as a result, a worse cell performance was observed for the cell with BSCF-3Ag electrode than that with pure BSCF electrode at 600 °C.