@inproceedings{4c2dc8a328654556a63121844c16a543,
title = "Strengthen of porous Al2O3 ceramics by adding nanoparticle ZrO2 addition",
abstract = "In this paper, Nanoslurry-ZrO2 were added into alumina powders to improve the bending strength of macroporous AI2O3 Ceramic sintered at 1550°C, 1600°C, 1650°C corresponding for3h each in air, respectively. The results show that the bending strength of porous alumina ceramic was simultaneously greatly influenced by various ZrO2 contents. When ZrO2 content is 2wt%, the maximum bending strength value of sample heated at 1650°C was observed, which achieves to 50 MPa. And the maximum bending strength value of any sample also exists at 1650°C By SEM analysis, many fine ZrO2 particles with high activity surface form a neck bonding which is beneficial to the improvements of bending strength.",
keywords = "Bending strength, Macroporous ceramic, Nanoslurry Zro, Wet-ball-milling",
author = "Gaiye Li and Yiqun Fan",
year = "2009",
doi = "10.4028/www.scientific.net/AMR.79-82.239",
language = "英语",
isbn = "0878493042",
series = "Advanced Materials Research",
pages = "239--242",
booktitle = "Multi-Functional Materials and Structures II",
note = "2nd International Conference on Multi-Functional Materials and Structures, MFMS-2009 ; Conference date: 09-10-2009 Through 12-10-2009",
}