Y and Fe co-doped LaNiO₃ perovskite as a novel bifunctional electrocatalyst for rechargeable zinc-air batteries

Perovskite oxides are widely regarded as the promising air electrode catalytic materials for zinc-air batteries (ZABs). In the present work, A-site Y and B-site Fe co-doped La_0.85Y_0.15Ni_0.7Fe_0.3O₃ perovskite catalyst was prepared by self-propagating high-temperature synthesis, and this material was evaluated as a bifunctional electrocatalyst for ZABs. The effect of co-doping on crystal structure and reaction activities, which can promote oxygen reduction reaction (ORR) and oxygen evolution reaction (OER), was investigated. Results show that Y and Fe co-doping substantially improved the ORR and OER of LaNiO₃. In comparison with LaNiO₃, the ORR performance of La_0.85Y_0.15Ni_0.7Fe_0.3O₃ exhibited a higher limiting current density (3.8 mA cm⁻² at 0.4 V vs. RHE) and more positive onset potential (0.75 V vs. RHE) at 1600 rpm. It also had an excellent OER performance of 1.74 V vs. RHE at 10 mA cm⁻². When La_0.85Y_0.15Ni_0.7Fe_0.3O₃ was used as an air electrode catalyst for ZABs, it exhibited a high power density of 93.6 mW cm⁻², which increased by 84.8% compared with that of LaNiO₃. Moreover, the full cell with La_0.85Y_0.15Ni_0.7Fe_0.3O₃ air electrode catalyst was operated for more than 80 h, maintaining good stability. Therefore, La_0.85Y_0.15Ni_0.7Fe_0.3O₃ can be used as a promising bifunctional air electrode catalyst for ZABs. The characterization analysis reveals that A-site Y and B-site Fe co-doped catalyst transforms crystal structure from trigonal system to cubic system, retain the valence state of Ni³⁺ and increases the contents of O₂²⁻/O⁻, and these properties are more conducive for LaNiO₃ catalysis.