Preparation of poly (butyl acrylate) and sulfonated polystyrene ionomer hybrid emulsion

Ping Wei; Hao Pang; Bing Liao

Preparation of poly (butyl acrylate) and sulfonated polystyrene ionomer hybrid emulsion

Ping Wei, Hao Pang, Bing Liao

CAS - Guangzhou Institute of Chemistry

科研成果: 期刊稿件 › 文章 › 同行评审

摘要

In this work, the polystyrene was modified to sulfonated polystyrene ionomer (SPS) and was emulsified to a stable polymer waterborne emulsion by using the technology of phase inversion. The internal of SPS particles in SPS waterborne emulsion was used as reaction area for the monomer butyl acrylate (BA) and the PBA/SPS hybrid emulsion has been prepared by this new technology. The factors that affect on the conversion of monomer and the diameter distribution of hybrid emulsion were studied. The morphology and the size of the hybrid emulsion particles were analysed by FT-IR and TEM.

源语言	英语
页（从-至）	150-153
页数	4
期刊	Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering
卷	21
期	2
出版状态	已出版 - 3月 2005
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{fce9f381c86e488f8ca3f342e235eb74,

title = "Preparation of poly (butyl acrylate) and sulfonated polystyrene ionomer hybrid emulsion",

abstract = "In this work, the polystyrene was modified to sulfonated polystyrene ionomer (SPS) and was emulsified to a stable polymer waterborne emulsion by using the technology of phase inversion. The internal of SPS particles in SPS waterborne emulsion was used as reaction area for the monomer butyl acrylate (BA) and the PBA/SPS hybrid emulsion has been prepared by this new technology. The factors that affect on the conversion of monomer and the diameter distribution of hybrid emulsion were studied. The morphology and the size of the hybrid emulsion particles were analysed by FT-IR and TEM.",

keywords = "Hybrid waterborne emulsion, Ionomer, SPS, Waterborne emulsion",

author = "Ping Wei and Hao Pang and Bing Liao",

year = "2005",

month = mar,

language = "英语",

volume = "21",

pages = "150--153",

journal = "Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering",

issn = "1000-7555",

publisher = "Chengdu University of Science and Technology",

number = "2",

}

TY - JOUR

T1 - Preparation of poly (butyl acrylate) and sulfonated polystyrene ionomer hybrid emulsion

AU - Wei, Ping

AU - Pang, Hao

AU - Liao, Bing

PY - 2005/3

Y1 - 2005/3

N2 - In this work, the polystyrene was modified to sulfonated polystyrene ionomer (SPS) and was emulsified to a stable polymer waterborne emulsion by using the technology of phase inversion. The internal of SPS particles in SPS waterborne emulsion was used as reaction area for the monomer butyl acrylate (BA) and the PBA/SPS hybrid emulsion has been prepared by this new technology. The factors that affect on the conversion of monomer and the diameter distribution of hybrid emulsion were studied. The morphology and the size of the hybrid emulsion particles were analysed by FT-IR and TEM.

AB - In this work, the polystyrene was modified to sulfonated polystyrene ionomer (SPS) and was emulsified to a stable polymer waterborne emulsion by using the technology of phase inversion. The internal of SPS particles in SPS waterborne emulsion was used as reaction area for the monomer butyl acrylate (BA) and the PBA/SPS hybrid emulsion has been prepared by this new technology. The factors that affect on the conversion of monomer and the diameter distribution of hybrid emulsion were studied. The morphology and the size of the hybrid emulsion particles were analysed by FT-IR and TEM.

KW - Hybrid waterborne emulsion

KW - Ionomer

KW - SPS

KW - Waterborne emulsion

UR - http://www.scopus.com/inward/record.url?scp=16644382758&partnerID=8YFLogxK

M3 - 文章

AN - SCOPUS:16644382758

SN - 1000-7555

VL - 21

SP - 150

EP - 153

JO - Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering

JF - Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering

IS - 2

ER -

Preparation of poly (butyl acrylate) and sulfonated polystyrene ionomer hybrid emulsion

摘要

其它文件与链接

指纹

引用此